3:1 Heavy Wall Polyolefin Hot Melting Heat Shrinkable Tubing/Tube Flypower-BH-RA3 manufacturer from China Flypower New Material Co., Ltd.

3:1 Heavy Wall Polyolefin Hot Melting Heat Shrinkable Tubing/Tube

Price:	1.0~10.0 USD
Payment Terms:	T/T,T/T
Place of Origin:	Guangdong, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: Flypower-BH-RA3

Production Capacity: 10,000,000

Delivery Date: within 7 days

Material: Stainless Steel

Characteristic: 3. Heavy wall, Semi-rigid, ...

Minimum fully recovery tempertature: 120C

Colors: Black, Red

Means of Transport: Land,Land

Packing: cartons

Type: R Type

Brand Name: Flypower

Shrink ratio: 3:1

Approvals: RoHS

Semi-rigid Hot-melt Adhesive Heavy Wall Heat Shrinkable Sleeve
3X Heavy Wall Polyolefin Hot-melt Heat Shrinkable Tube BH-RA3
HEAT SHRINKABLE HEAVY W

Heavy wall heat shrinkable tube (with adhesive)

Structure:

Heavy wall heat shrink tube is manufactured by co-extrusion polyolefin and environment friendly hot-melt adhesive. Designed to provide both insulation and sealing for protected.

Application:

Semi-rigid heavy wall polyolefin heat shrinkable tubing with hot melting adhesive protecting electrical splices, cable terminations and joints where electrical Insulation and waterproof are required.

Characteristics:

1.Shrink ratio:3:1

2.Minimum fully recovery tempertature:120C

3.Heavy wall, Semi-rigid, Insulate, and excellent sealing performance

4.Approvals: RoHS

5.Colors: Black, Red

Specification:

Normal size (mm)	As supplied (mm)	After recovered (mm)		*Style	Standard length (mm)
Normal size (mm)	Inside diameter (min.)	Inside diameter (Max.)	Wall thickness (mm)	*Style	Standard length (mm)
9/3	9	3	1.8	O	1000-1500
13/4	13	4	2.4	O	1000-1500
22/6	22	6	2.7	O	1000-1500
33/8	33	8	3.2	O	1000-1500
40/12	40	12	4.1	O	1000-1500
45/12	45	12	4.1	O	1000-1500
55/16	55	16	4.1	O	1000-1500
75/22	75	22	4.1	O	1000-1500
85/25	85	25	4.3	O	1000-1500
95/30	95	30	4.3	O	1000-1500
105/30	105	30	4.3	O	1000-1500
130/36	130	36	4.3	—	1000-1500
160/50	160	50	4.3	—	1000-1500
180/50	180	50	4.3	—	1000-1500
200/60	200	60	4.3	—	1000-1500

Technical Data:

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55 to +110℃
Tensile strength	ASTM D2671	≥14MPa
Tensile strength after aging	ASTM D 2671/150℃, 168hrs.	≥12MPa
Elongation at break	ASTM D2671	≥400%
Elongation at break after aging	150℃ ,168hrs	≥300%
Density	ASTM D792	1.05g/cm3
Longitudinal shrinkage	UL224	0 to -10%
Dielectric strength	IEC243	≥20kV/mm
Volume resistance	IEC93	≥1014ΩNaN
Eccentricity	ASTM D2671	<30%
Copper stability	ASTM D2671	Pass
Resistance to stress cracking (50℃)	ASTM D1693	No Cracking
Water absorption	ISO 62/23℃,14days	<0.15%
Softening point	ASTM D E8	85℃
Peel strength (PE)	DIN 30672	4 N/cm
Copper stability	ASTM D 2671	Non-corrosive
Resistance to fungus and decay	ISO 846	Pass